浙江國森精細化工科技有限公司

Product Name

Color

Viscosity, cps

Solid

content

Weight

ratio

Initial

curing   time

Curing

condition

Characteristics and Application

EP912

A: Yellow viscous fluid

B: Yellow semi-transparent viscous fluid

A:5,000~15,000

B:200~1,000

100%

A:B=3:1

8hr (10 g)

Atmospheric

temperature

A two-component solvent-free   environmentally acceptable floor adhesive. Ithas such advantages as handling   convenience, long application time, curing at room temperature,nofoaming, no sagging, and storage   stability.After   cured, it has goodresistance   to impact and water, and high adhesion to various substrates. It can be   widely used to bond wood, metal, concrete, rubber, PVC, ceramics, etc.

EP100

A: Milky white viscous fluid

B: Yellow semi-transparent viscous fluid

A:8,000~20,000

B:100~500

100%

A:B=3:1

8hr   (10 g)

Room

temperature

A two-component high temperature   resistant repair adhesive which can be cured at room temperature. It has the   characteristics of simple preparation, high temperature resistance, good   impact resistance, good wettability, and high adhesion. It can bond wood, carbon   fiber cloth, and metal very well.It   can cure at room temperature and resist the temperature above 100 ℃.

EP918

A: Viscous fluid, color determined by   customers

B: Yellowish brown transparent viscous   fluid

A:10,000~40,000

B：20,000~65,000

100%

A:B=1:1

50 min (10 g)

Room temperature or medium temperature

An epoxy adhesive which can cure at room   temperature or medium temperature. It has the characteristics of simple preparation,   high bonding strength, and good impact resistance. Especially, the color   which matches with wood can be selected by customers. It overcomes the common   blackening phenomenon after wood lamination and painting. It is specifically   used for lamination and bonding of various wood on yachts, and strong bonding   of metal, glass, ceramics, stone, hard plastics, FRP, wood, etc.

Product Name

Color

Viscosity, cps

Solid content

Weight ratio

Environmental   standard

Characteristics   and Application

EP199

Black

2,000~8,000 after   mixing of A and B

100%

A:B=4:1

RoHSREAC

An   epoxy pouring sealant which cures at room temperature. Due to its simple   preparation, high bonding strength, good heat resistance, good electrical   insulation, good air tightness, good resistance to cold and heat shock, etc.,   it is widely used to pour electronic components with high air tightness and   high temperature resistance.

EP198

Black

3,000~9,000 after   mixing of A and B

100%

A:B=6:1

RoHSREAC

A   two-component epoxy pouring sealant which cures at normal temperature or high   temperature. Due to its simple preparation, high bonding strength, excellent   heat resistance, good electrical insulation, good air tightness, good resistance   to cold and heat shock, it is widely used to pour electronic components with   high air tightness and resistance to high temperature above 250℃.

EP118

Black

A:20,000~40,000

B:5~100

100%

A:B=10:1

RoHSREAC

A two-component thermal conductive epoxy   electronic pouring sealant which cures at room temperature. It has long pot   life, mild temperature impact, small shrinkage, good operability,   permeability and wettability. After cured, it has good surface gloss, few bubbles,   high adhesion and mechanical strength. It can bond PBT, PVC, etc. It has good   resistance to cold and heat shock, and good electrical performance. It is   suitable for sealing of electronic components with the above requirements.

EP460

Light amber

20,000~30,000   after mixing

100%

A:B=2:1

RoHSREAC

It is   suitable for low stress and general industrial applications at high impact   strength and high peel strength. It can be widely used for aluminum, steel,   and other metals, as well as various plastics and ceramics.

EP146

Black

A:9,000~13,000

B:5~100

100%

A:B=4:1

RoHSREAC

A   two-component epoxy electronicpouring   sealant which cures at room temperature or at medium temperature. It has long   pot life, mild temperature impact, small shrinkage, good operability,   permeability, and wettability. After cured, it has good surface gloss, few   bubbles, high bonding strength and mechanical strength. It can bond PVC. It   has good resistance to cold and heat shock, good electrical performance, and   good resistance to boiling.It   is suitable for sealing of electronic components with the above requirements.

Product Name

Color

Viscosity, cps

Solid content

Weight ratio

Initial   curing time

Characteristics   and Application

EP980

Milky white

A:20,000~50,000 CP

B:10,000~40,000 CP

100%

A:B=1:1

5 min

(10 g)

A   two component epoxy adhesive which can quickly cure in five minute quick   dryings. Due to its characteristics, such as simple preparation, high bonding   strength, good impact resistance, and good low-temperature curing properties,   it is widely used for strong bonding of metals, glass, ceramics, stone, hard   plastics, FRP, wood, etc., especially DIY products.

EP120

Water clear

A:1,000~3,000 CP

B:5~100 CP

100%

A:B=3:1

/

A   two-component transparentpouring   sealant which cures at room temperature. Due to its high transparency,resistance to yellowing, and good   defoaming performance, it is suitable for transparent pouring andhandicraft production.

EP195

A: Black viscous fluid

B: Yellow viscous fluid

A:1,000,000~2,000,000 CP

B:500,000~1,500,000 CP

100%

A:B=2:1

/

A two-component epoxy adhesive which   cures at room temperature or high temperature. Due to its characteristics,   such as simple preparation, high bonding strength, good heat resistance,   corrosion resistance, and impact resistance, it is widely used for metals,   glass, ceramics, stone, hard plastics, FRP, wood, and other materials with   high temperature resistance.

Product   

Name

Color

Viscosity

cps

Solid   

content

Weight

ratio

Initial

curing   

time

Curing   

conditions

Shear   

strength,MPa

Hardness

Shore D

Characteristics   and Application

GU302

Light   yellow viscous fluid

10,000

≥99%

A:B=4:1

120min

(10 g)

Twocomponents mixed and cured at room temperature

8

45

An   adhesive used for civil construction. It can bond rubber floor, wood, gypsum   board, steel plate, PU foam material, rock wool board, and PVC board very   well.

GU803

Light   yellow viscous fluid

600,000

≥99%

A:B=5:1

90min

(10 g)

Twocomponents mixed and cured at room temperature

≥1

70

Adhesive   used for civil construction. It is suitable for flooring in gymnasium,   schools, homes, etc. It can bond various substrates such as PVC and rubber   flooring very well.

GU802

Light   yellow viscous fluid

500,000

≥99%

A:B=51

90min

(10 g)

Twocomponent mixed and cured at room temperature

≥10

70

An   adhesive used in civil construction. It bonds various substrates such as PVC,   rubber, wood, epoxy flooring, metal, and cement very well.

GU512（H）

Light   yellow viscous fluid

50,000

≥99%

One-component

150min

(10 g)

25 ℃, RH=50%

≥8

65

An   adhesive used in buildings. It has high strength and good elasticity. It can   be used to bond metal, plastics, rubber, fiber, wood, glass, spongefoam, ceramics, etc.

Product   Name

Appearance   

Viscosity,   cps

Solid   content

Weight   ratio

Environmental   standard

Characteristics   and Application

GU805

Biege

12,000 ±   4,000 CP

≥99%

A:B=4:1

RoHS\

REACH

A two-component   polyurethane electronic pouring adhesive. It has good adhesion to various substrates   such as PVC and inorganic substrates.

Product   

Name

Color

Viscosity,   cps

Solid   content

Characteristics   and Application

CE105

White   thick latex

15,000~40,000

≥36%

A   polyvinyl acetate polymer. It can bond wood, plywood, paper, cloth, leather,   bamboo, etc.

CE125

White   thick latex

18,000~23,000

≥18%

A   polyvinyl acetate polymer. It can bonf wood, veneer, paper, cloth, bamboo,   etc.

CE135

White   thick latex

120,000~180,000

≥35%

A   polyvinyl acetate polymer. It can bond wood, veneer, paper, cloth, bamboo,   etc.

CE145

White   thick latex

8,000~15,000

≥40%

A   polyvinyl acetate polymer. It is used as one-component high-strength adhesive   for civil construction.

Product Name

Color

Viscosity

cps

Solid

content

Characteristics and Application

CA381

milky white

2,000±500

50%±1

A one-component tile adhesive prepared by special modified polymer   emulsion. It is easily used. It can effectively improve the bonding strength   between polished tiles and bonding mortar, and solve the common problems of   hollowing and peeling in polished tiles. It has excellent water resistance, and   is extremely suitable for dense stone and ceramic tiles with low water   absorption.

CA388

White transparent

3,000±1,000

40%±1

A transparent waterproof adhesive for exterior walls. It is made by a   special polymerization process. Its coating has excellent waterwhite resistance, wet adhesion, transparency, inability   to affect the original effect of the building, non-stickiness, and flexibility.   Due to high-quality raw materials, the coating has excellent aging resistance   and weather resistance, and good workability. It has good coverage on tile   surfaces and joints and never shrinks. After cured, the coating forms a   transparent elastic waterproof protective film, which is an ideal protective   waterproof material for various types of building surfaces.

CA375

milky white

yellow

green

1500±500

12-15%

It has strong permeability, good sealing effect, high bonding strength,   non-toxicity, no odor, safety and environmentally acceptability. It is suitable   for application ofputty to concrete, brick walls, and cement mortar or interface   treatment beforeplastering and roughening   ofsmooth walls. It can   effectively prevent hollowing, cracking, and powdering of the wall leveling   layer, and improve the bonding strength between putty or mortar and the wall.

CA512

Light blue lotion

50~250

≥48%

A polyacrylate emulsion used for prevention of water and leak.

CA560

White, light gray

Paste, >50,0000

＞70%

An elastic emulsion suitable for caulking of indoor or outdoor building   materials that do not directly contact with water. It has paint resistance,   safety and Environmental standard, beautifies edges and seams and prevents cracks.

CA688

Light yellow

15,000~25,000

＞70%

It isdevelopedfor bonding of PVCflooring. It is suitable for PVC rolls and PVC blocks,   including homogeneous and permeablePVCflooring, anti-slip flooring and sound insulation   flooring with foam lining, especially for thick flooring.

CA588

Light yellow viscous fluid

15,000~

38,000

≥71%

It isdevelopedfor bonding of PVC flooring materials. It is suitable   for bonding of PVC rolls for flooring, especially for thick flooring.

CA888

Light yellow viscous fluid

＞50,000

＞70%

A one-component adhesive for   rubber floor, PVC rolls, walls, stairs, and other plastics floors.

CA810

Milky white

5,000~10,000

≥52%

A polymer emulsion designed for PVC flooring. It has good construction   operability and bonding performance, strong initial adhesion, long application   time. It can be applied on various absorbent or non absorbent substrates,   with stable performance.

CA510E

Milky white with blue light

25,000~35,000

≥53%

A polymer emulsion specially designed for PVC flooring. It has good   bonding strength and pressure sensitivity, especially outstanding initial   adhesion. It has good resistance to water, solvent and low temperature, ease   to use, and stable performance.

Product Name

Color

Viscosity, s

Solid content

Gloss

Wear resistance

Characteristics and Application

CA310

Milky white liquid

15~30

40~45%

>75

＞ 100 times

CA310 is a water-based spraying varnish. It is mainly used for surface varnish   finish and protection of paper, wood, etc. It has fast curing rate, good   transparency, high gloss, good waterproofing property, low odor, no irritability,   and Environmental standard. It can effectively replace solvent-based varnish   products and never cause environmental pollution and harm to human health.

CA311

Milky white liquid

20~50

35~40%

>60

>100 times

It is water-based brushing varnish. It is mainly used for surface gloss   and protection of paper, wood, etc. It has fast curing rate, good   transparency, high gloss, good waterproofing property, low odor, no irritability,   and green and Environmental standard. It can effectively replace solvent-based   varnish products and never cause environmental pollution and harm to human   health.

CA302

Milky white liquid

35~45

41-45%

60~70

>100 times

CA302 is an infrared radiation cured water-based varnish with high gloss   and wear-resistance. It is mainly used for varnish finish of paper and   printed products to increase the surface gloss of printed products, wear   resistance and surface smoothness and protect ink. It has fast curing rate,   high production efficiency, low odor, no irritability, and never causes   environmental pollution. Its coating is very glossy, resistant to wear, flat,   smooth, resistant to yellowing, fast finished,firm, uniform, foldable, etc.

Product   

Name

Color

Viscosity,

cps

Surface   

junction

Skin time

Curing

condition

Shear   

strength,

MPa

Hardness

Shore D

Characteristics   and Application

MS405

White

Pasty

3 h

Water

/

40

A one-component   neutral modified silicone. It can be cured   by its reactionwithwater in air.It has excellent performance and can bond most materials without any   primer. It has excellent resistance to weather, UV,heatand cold, and excellent adhesiontovarious building materials. Anenvironmentally acceptable adhesivewith very low VOC.

MS450

Brown

800,000

30 min

Water

≥1.5

65

An elastic   adhesive for flooring. It is specially designed for bonding of various   flooring surfaces such as cement, tile, marble, quartz tiles, and wooden   floor to provide excellent adhesion, elasticity, noise resistance, moisture   resistance, and ability to match with indoor colors. It contains no   formaldehyde or VOC. An environmentally acceptable elastic adhesive for   indoor decoration and flooring.

Product   

Name

Color

Viscosity,   

cps

Curing   

type

Applicable

occasions

Characteristics   and Application

UV710S

Slightly   yellow translucent paste

30,000~80,000

UV + heat   

Dual-curable   frame adhesive for plastics substrate in screen printing process

A single-component   UV + heat curedLCD frame adhesive forscreenprinting process. It has good defoaming   and leveling properties.Afterscreen printing and bonding, it always generates nobubbles,hasstrong adhesion toplastics substrates,goodelectrical properties, flexibility, and   low ion content, and never affects the characteristics of liquid crystals.

UV710F

Slightly   yellow translucent paste

120,000~20,0000

UV + heat   

Dual-curable   frame adhesive forplasticssubstrate in ODFprocess

A one-component   UV+ heat cured LCD frame adhesiveused in the ODFprocess. It hasstrong adhesionto the substrate,good flexibility, low ion content, and never   contaminates liquid crystalbefore and aftercured.

UV770F

Slightly   yellow translucent paste

10,0000~20,0000

UV

Water-cured   frame adhesive

It is one-component   UV cured EWD frame adhesiveused in the ODFprocess. It has simple curing method, fast curing rate,good sag resistance, strong adhesion toplastics substrates,goodelectrical properties,good flexibility, low ion content, and   incompatibility with waterbefore and aftercured.

Product

Name

Separation

conditions

Viscosity,

cps

Solid

content

Applicability to

Product Features

Application

BA516

Low-temperature

150~600

25~35%

Temporary bonding between plastics and glass

Good heat resistance, strong adhesion, ease to peel off   at low temperatures, and no residual adhesive after peeling

A single-component   low-temperaturedebondtype handling adhesive. It is suitable for   bonding and separation between thin glass and thick glass substrates. Always applied   by slot die coater. It has high transparency,goodheatresistance, and enough strength to fix   the plastics substrate in general manufacturing processes. It is easily peeled   off at lowtemperatures,   without residual adhesive. It has high UV penetration rate, and neveraffects the subsequent curing of the   frame adhesive.

BA513

Low-temperature

150~600

25~35%

Temporary connection between thin glass and thick glass   substrate

Good heat resistance, strong adhesion, ease to peel off   at low temperatures, and no residual adhesive after peeling

A single-component low-temperaturedebondtype handling adhesive. It   is suitable for bonding and separation between substrates with significant   CTE differences.Always applied by slot die   coater. It has high transparency,goodheatresistance, and enough   strength to fix the plastics substrate in general manufacturing processes. It   is easily peeled off at lowtemperatures, without   residual adhesive. It has high UV penetration rate, and neveraffects the subsequent curing of the frame adhesive.

BU220

UV

200~1800

25~35%

Temporary connection betweentransparent plastics substrateand vehicle substrate

Good heat resistance, strong adhesion, ease to peel   after UV curing, and no residual adhesive after peeling

A single-component UVbondedhandling adhesive. It is suitable fortemporary bonding betweentransparent plastics substratesand vehicle substrates.Always applied by slot die coater. It has high   transparency, good heat resistance, and enough strength to fix the plastics   substrate in general manufacturing processes. After UV cured, it is easily peeled   off, without residual adhesive.